The Risi SCT1300 steel strip is made of hardened carbon steel and has the following characteristics:
u Excellent static strength
u Excellent wear resistance
u Excellent fatigue strength
u Good maintainability
u Excellent thermal conductivity
The hard, smooth surface and black oxide coating of CT1300 make it suitable for any application with low corrosion risk. Excellent thermal conductivity makes it ideal for baking and heating and drying liquids, pastes and fine products.
Chemical composition (nominal value)
|
carbon c |
Silicon Si |
Manganese Mn |
Phosphorus P |
Sulfur s |
Chromium Cr |
Copper Cu |
Nickel Ni |
aluminium Al |
cutter Fe |
|
0.30 |
0.24 |
1.00 |
＜0.03 |
0.002 |
0.22 |
0.02 |
0.01 |
0.022 |
- |
Static strength
Standard strength at room temperature (nominal value)
|
parameter |
tensile strength |
yield strength |
Elongation rate |
welding coefficient |
hardness |
||
|
|
Mpa |
Ksi |
Mpa |
Ksi |
A5(%) |
Rm/Rm |
HV5 |
|
Base material |
1250 |
181 |
1100 |
160 |
10 |
* |
380 |
|
Welding area |
1000 |
145 |
950 |
138 |
4 |
0.75 |
* |
scope of supply
|
Length: customizable |
|
width:600/800/1000/1200/1500/ …mm |
|
thickness:0.8/1.2/1.4/1.5 mm |
|
Prompt: The maximum width of a single steel strip is 1500 mm, and longitudinal splicing is required if the width exceeds this width. Special specifications can be customized. |
*The data in this document is representative but not absolutely guaranteed. The data can also vary from batch to batch.